Hastelloy C2000 Fasteners

Hastelloy C2000 Fasteners

Hastelloy C2000 Fasteners exhibit exception resistant to sulphuric acid along with hydrchloric anc hydrofluoric acids. This alloy has a deliberate copper addition which enhances its resistance to sulfuric acid to great extent. Boltport Fasteners offers all types of bolts, screws, stud bolts, threaded rods, nuts, washers and custom bolting in Hastelloy C2000.

Hastelloy® C2000

The technical objective of the design of Hastelloy C-2000 was even greater versatility, as compared with the traditional Ni-Cr-Mo alloys. This was accomplished by use of a high chromium content (23%), a high molybdenum content (16%), and a small but effective addition of copper (1.6%). The copper was found to provide enhanced temperature capability in sulfuric acid, hydrofluoric acid, and dilute hydrochloric acid. A Ni-Cr-Mo-W alloy, C-22 offers resistance to pitting, stress-corrosion cracking, and crevice corrosion.

Hastelloy C2000 Technical Data Sheet

Hastelloy C2000 Fasteners

  • Hastelloy C2000 Bolts
  • Hastelloy C2000 Screws
  • Hastelloy C2000 Stud Bolts
    Stud Bolts
  • Hastelloy C2000 Threaded Rods
    Threaded Rods
  • Hastelloy C2000 Nuts
  • Hastelloy C2000 Washers
  • Springs
  • Pins
  • Hastelloy C2000 Accessories
  • Hastelloy C2000 Components

Hastelloy C2000 Equivalent Grades

xxx xxx xxx
Alloy C2000 UNS N06200 DIN 2.4675

Hastelloy C2000 Properties

Hastelloy B2 Chemical Composition

Molybdenum Chromium Iron Cobalt Carbon Silicon Manganese Phosphorus Sulphur Nickel Aluminium Copper
15.0 - 17.0 % 22.0 - 24.0 % 3.00 % max 2.00 % max 0.01 % max 0.08 % max 0.50 % max 0.025 % max 0.01 % max Balance 0.50 % max 01.30 - 1.90 %

Hastelloy C2000 Mechanical Properties

Tensile Strength Yield Strength Elongation at break Hardness, Brinell
690 MPa 310 MPa 45% ...

Hastelloy C2000 Specifications

Specifications Description Additional Details
ASTM B462   More Information »
ASTM B574   More Information »