This specification covers requirements for commercial wrought non ferrous nuts from diameter 1/4 inch to 1-1/2 inch inclusive manufactured from variety of Copper alloys, Monel alloy 400, 405, K500, Inconel 625, Aluminum alloys and Titanium as well, intended for general service applications. BoltPort manufactures most of the alloy bolting cover under ASTM F467(Imperial) and F4677(Metric) with coarse and fine threads. All the bolt and screw products are duly tested and supplied with EN 10204 Type 3.1 certification.
| Alloy | Condition |
|---|---|
| All Alloys in Copper | As formed or stress relieved at manufacturer's option |
| Nickel Alloys: | |
| Monel 400 and Monel 405 | As formed or stress relieved at manufacturer's option |
| Monel K500 | Solution annealed and aged |
| Inconel 625 | Annealed |
| Aluminum Alloys: | |
| 2024-T4 | Solution treated and naturally aged |
| 6061-T6 | Solution treated and artificially aged |
| 6262-T73 | Solution treated and stablilized |
| Titanium | As Formed |
| Composition, % Copper and Copper Base Alloys |
|||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| UNS Designation | Alloy | General Name | Aluminum | Copper, min | Iron, max | Manganese, max | Nickel, max | Phosphorus | Silicon | Zinc, maxA | Lead, max | Tin | Arsenic, max |
| C11000 | 110 | ETP Copper | -- | 99.9 | -- | -- | -- | -- | -- | -- | -- | -- | -- |
| C26000 | 260 | Brass | -- | 68.5 - 71.5 | 0.05 | -- | -- | -- | -- | balance | 0.07 | -- | -- |
| C27000 | 270 | Brass | -- | 63.0 - 68.5 | 0.07 | -- | -- | -- | -- | balance | 0.10 | -- | -- |
| C46200 | 462 | Naval Brass | -- | 62.0 - 65.0 | 0.10 | -- | -- | -- | -- | balance | 0.20 | 0.50 - 1.00 | -- |
| C46400 | 464 | Naval Brass | -- | 59.0 - 62.0 | 0.10 | -- | -- | -- | -- | balance | 0.20 | 0.50 - 1.00 | -- |
| C51000 | 510 | Phosphor Bronze | -- | balanceA | 0.10 | -- | -- | 0.03 - 0.35 | -- | 0.30 | 0.05 | 4.20 - 5.80 | -- |
| C61300 | 613 | Aluminum Bronze | 6.0 - 7.5 | B | 2.0 - 3.0 | 0.10 | 0.15C | 0.015 | 0.10 | 0.05 | 0.01 | 0.20 - 0.50 | -- |
| C61400 | 614 | Aluminum Bronze | 6.0 - 8.0 | 88.0D | 1.5 - 3.5 | 1.00 | -- | -- | -- | -- | -- | -- | -- |
| C63000 | 630 | Aluminum Bronze | 9.0 - 11.0 | 78.0D | 2.0 - 4.0 | 1.50 | 4.0 - 5.5 | -- | 0.25 max | -- | -- | 0.20 max | -- |
| C64200 | 642 | Aluminum Silicon Bronze | 6.3 - 7.6 | 88.65D | 0.30 | 0.10 | 0.25 | 1.50 - 2.20E | 0.50 | 0.05 | 0.20 max | 0.15 | |
| C65100 | 651 | Silicon Bronze | -- | 96.0D | 0.80 | 0.70 | -- | -- | 0.8 - 2.0 | 1.50 | 0.05 | -- | -- |
| C65500 | 655 | Silicon Bronze | -- | 94.8D | 0.80 | 1.50 | 0.60 | -- | 2.8 - 3.8 | 1.50 | 0.05 | -- | -- |
| C66100 | 661 | Silicon Bronze | 0.25 max | 94.0D | 0.25 | 1.50 | -- | -- | 2.8 - 3.5 | 1.50 | 0.20 - 0.80 | -- | -- |
| C67500 | 675 | Manganese Bronze | -- | 57.0 - 60.0 | 0.8 - 2.0 | 0.05 - 0.50 | -- | -- | -- | balance | 0.20 | 0.50 - 1.50 | -- |
| C71000 | 710 | Cupro Nickel | -- | 74.0D | 0.60 | 1.00 | 19.0 - 23.0C | -- | 1.00 | 0.05 | -- | -- | |
| C71500 | 715 | Cupro Nickel | -- | 65.0D | 0.40 - 0.70 | 1.00 | 29.0 - 33.0C | -- | -- | 1.00 | 0.05 | -- | -- |
A Elements shown as balance shall be arithmetically computed by deducting the sum of the other named elements from 100.
B Copper plus specified elements = 99.8 min; copper plus silver = 88.5-91.5.
C Cobalt is to be counted as nickel
D Minimum content of copper plus all other elements with specified limits shall be 99.5%.
E An alloy containing as high as 2.5% silicon is acceptable provided the sum of all the elements other than copper, silicon and iron does not exceed 0.30 %.
| Composition, % Nickel and Nickel Base Alloys |
|||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| UNS Designation | Alloy | General Name | Aluminum | Carbon, max | Chromium | CopperA | Iron, max | Manganese, max | NickelA | Phosphorus, max | Silicon, max | Titanium | Cobalt, max | Molybdenum | Sulfur, max | Vanadium | Tungsten |
| N10001 | 335 | Ni-Mo | -- | 0.05 | 1.00 max | -- | 4.00 - 6.00 | 1.00 | balance | 0.025 | 1.00 | -- | 2.50 | 26.0 - 30.0 | 0.030 | 0.20 - 0.40 | -- |
| N10276 | 276 | Ni-Mo-Cr | -- | 0.02 | 14.5 - 16.5 | -- | 4.00 - 7.00 | 1.00 | balance | 0.040 | 0.08 | -- | 2.50 | 15.0 - 17.0 | 0.030 | 0.35 max | 3.0 - 4.5 |
| N04400 | 400 | Ni-Cu Class A | -- | 0.30 | -- | balance | 2.50 | 2.00 | 63.0 - 70.0 | -- | 0.50 | -- | B | -- | 0.024 | -- | -- |
| N04405 | 405 | Ni-Cu Class B | -- | 0.30 | -- | balance | 2.50 | 2.00 | 63.0 - 70.0 | -- | 0.50 | -- | B | -- | 0.025 - 0.060 | -- | -- |
| N05500 | 500 | Ni-Cu-Al | 2.30 - 3.15 | 0.25 | -- | balance | 2.00 | 1.50 | 63.0 - 70.0 | 0.015 | 0.50 | 0.35 - 0.85 | B | -- | 0.010 | -- | -- |
| N06059 | 59 | Ni-Cu-Mo | 0.10 - 0.40 | 0.010 max | 22.0 - 24.0 | 0.50 max | 1.50 | 0.50 | balance | 0.015 | 0.10 | -- | 0.30 | 15.0 - 16.5 | 0.010 | -- | -- |
| N06625 | 625C | Ni-Cr-No-Cb | 0.40 max | 0.010 max | 20.0 - 23.0 | -- | 5.00 | 0.50 | 58.0 min | 0.040 | 0.50 | 0.40 max | 1.00 | 8.0 - 10.0 | 0.015 | -- | 3.2 - 4.2 |
| N06686 | 686 | Ni-Cr-Mo-W | -- | 0.010 max | 19.0 - 23.0 | -- | 5.00 | 0.50 | balance | -- | 0.08 | 0.02 - 0.25 | -- | 15.0 - 17.0 | 0.02 | -- | 3.0 - 4.4 |
A Elements shown as balance shall be arithmetically computed by deducting the sum of the other named elements from 100.
B Cobalt is to be counted as nickel.
C Alloy 625 material shall be refined using the electrostag remelting process (ESR), or the vacuum arc remelting process (VAR).
| Composition, % Aluminum Base AlloysA |
|||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| UNS Designation | Alloy | General Name | AluminumB | Chromium | Copper | Iron, max | Manganese, max | Silicon, max | Titanium, max | Zinc, max | Magnesium | Other Elements, max | |
| Each | Total | ||||||||||||
| A92024 | 2024 | Aluminum 2024 | balance | 0.10 max | 3.80 - 4.90 | 0.50 | 0.30 - 0.90 | 0.50 | 0.15C | 0.25 | 1.20 - 1.80 | 0.05 | 0.15 |
| A96061 | 6061 | Aluminum 6061 | balance | 0.04 - 0.35 | 0.15- 0.40 | 0.70 | 0.15 | 0.40 - 0.80 | 0.15 | 0.25 | 0.80 - 1.20 | 0.05 | 0.15 |
| A96262 | 6262 | Aluminum 6262 | balance | 0.18 - 0.35 | 1.20 - 2.00 | 0.50 | 0.30 | 0.40 | 0.20D | 5.10 - 6.10 | 2.10 - 2.90 | 0.05 | 0.15 |
A Analysis shall regularly be made only for the elements specified in this table. If, however, the presence of other elements is suspected or indicated in amounts greater than the specified limits, further analysis shall be made to determine that these elements are not present in excess of the specified limits.
B Elemens shown as balance shall be arithmetically computed by deducting the sum of the other named elements from 100.
C Titanium + Zirconium 0.20 %, max
D Titanium + Zirconium 0.25 %, max
| Composition, % Titanium and Titanium Base AlloysA |
|||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| UNS Designation | Alloy | General Name | Aluminum | Carbon | Iron | Titanium | Hydrogen | Nitrogen | Oxygen | Palladium | Vanadium | Chromium | Molybdenum | Zirconium | Tin | Silicon | Ruthenium | ResidualsB | |
| Each | Total | ||||||||||||||||||
| R50250 | 1 | Titanium Grade 1 | -- | 0.10 | 0.20 | balance | 0.0125 | 0.05 | 0.18 | 0.10 | 0.40 | ||||||||
| R50400 | 2 | Titanium Grade 2 | 0.10 | 0.30 | balance | 0.0125 | 0.05 | 0.25 | 0.10 | 0.40 | |||||||||
| R50700 | 4 | Titanium Grade 4 | 0.10 | 0.50 | balance | 0.0125 | 0.07 | 0.40 | 0.10 | 0.40 | |||||||||
| R56400 | 5C | Titanium grade 5C | 5.50 - 6.75 | 0.10 | 0.40 | balance | 0.0125 | 0.05 | 0.20 | 3.50 - 4.50 | 0.10 | 0.40 | |||||||
| R54601 | 23 | Titanium Ti-5Al-4V ELI | 5.50 - 6.50 | 0.08 | 0.25 | balance | 0.0125 | 0.05 | 0.13 | 3.50 - 4.50 | 0.10 | 0.40 | |||||||
| R52400 | 7 | Titanium Grade 7 | 0.10 | 0.30 | balance | 0.0125 | 0.05 | 0.25 | 0.12 - 0.25 | 0.10 | 0.40 | ||||||||
| R58640 | 19 | Titanium Ti-28-6-44 | 3.00 - 4.00 | 0.05 | 0.30 | balance | 0.0200 | 0.03 | 0.12 | 0.10D | 7.50 - 8.50 | 5.50 - 6.50 | 3.50 - 4.50 | 3.50 - 4.50 | 0.10D | 0.10 | 0.40 | ||
| R55111 | 32 | Titanium Ti-5-1-1-1 | 4.50 - 5.50 | 0.08 | 0.25 | balance | 0.0125 | 0.03 | 0.11 | 0.60 - 1.40 | 0.60 - 1.20 | 0.60 - 1.40 | 0.60 - 1.40 | 0.60 - 1.40 | 0.10 | 0.40 | |||
A All reported values are maximums, unless a range is specified.
B A residual is an element present in a metal or an alloy in small quantities inherent to the manufacturing process but not added intentionally. Residual elements need not be reported unless a report is specially required by the purchaser.
C Identical chemical requirements apply to both Class A and B as defined in Table 2 and 6.5 of ASTM F467.
D Ruthenium and palladium, or both, may be added to Grade 19 for enhanced corrosion resistance as negotiated between purchaser and vendor. Chemical analysis is not required unless specifically required by the purchaser.
| Alloy | Mechanical Property Marking | Nominal Thread Diameter, inch | HardnessA | Proof Stress, min, ksi |
|---|---|---|---|---|
| Copper | ||||
| Cu 110 | F 467A | all | 65 HRF | 30 |
| Cu 260 | F 467AB | all | 55 HRF | 60 |
| Cu 270 | F 467B | all | 55 HRF | 60 |
| Cu 462 | F 467C | all | 65 HRB | 50 |
| Cu 464 | F 467D | all | 55 HRB | 50 |
| Cu 510 | F 467E | all | 60 HRB | 60 |
| Cu 613 | F 467F | all | 70 HRB | 80 |
| Cu 614 | F 467G | all | 70 HRB | 75 |
| Cu 630 | F 467H | all | 85 HRB | 100 |
| Cu 642 | F 467J | all | 75 HRB | 75 |
| Cu 651 | F 467K | all | 75 HRB | 70 |
| Cu 655 | F 467L | all | 60 HRB | 50 |
| Cu 661 | F 467M | all | 75 HRB | 70 |
| Cu 675 | F 467N | all | 60 HRB | 55 |
| Cu 710 | F 467P | all | 50 HRB | 45 |
| Cu 715 | F 467R | all | 60 HRB | 55 |
| Nickel Alloys | ||||
| Ni 59 Grade 1 | F467FN | all | 21 HRC | 120 |
| Ni 59 Grade 2 | F467GN | all | 23 HRC | 135 |
| Ni 59 Grade 3 | F467HN | all | 25 HRC | 160 |
| Ni 59 Grade 4 | F467JN | all | 80 HRB | 100 |
| NI 335 | F 467S | all | 20 HRC | 115 |
| Ni 276 | F 467T | all | 20 HRC | 110 |
| Ni 400 | F 467U | all | 75 HRB | 80 |
| Ni 405 | F 467V | all | 60 HRB | 70 |
| Ni 500 | F 467W | all | 24 HRC | 130 |
| Ni 625 | F 467AC | all | 85 HRB - 35 HRC | 60 |
| Ni 686 Grade 1 | F 467BN | all | 21 HRC | 120 |
| Ni 686 Grade 2 | F 467CN | all | 23 HRC | 135 |
| Ni 686 Grade 3 | F 467DN | all | 25 HRC | 160 |
| Ni 686 Grade 4 | F 467EN | all | 65 HRB - 25 HRC | 100 |
| Aluminum | ||||
| Al 2024 - T4B | F 467X | all | 70 HRB | 55 |
| Al 6061 - T6 | F 467Y | all | 40 HRB | 40 |
| Al 6262 - T9 | F 467Z | all | 60 HRB | 52 |
| Titanium Alloys | ||||
| Ti 1 | F 467AT | all | 140 HV | 40 |
| Ti 2 | F 467BT | all | 150 HV | 55 |
| Ti 4 | F 467CT | all | 200 HV | 85 |
| Ti 5 | F 467DT | all | 30 HRC | 135 |
| Ti 7 | F 467ET | all | 160 HV | 55 |
| Ti 19 | F 467FT | all | 24 HRC | 120 |
| Ti 23 | F 467GT | all | 25 HRC | 125 |
| Ti-5-1-1-1 | F 467AHT | all | 24 HRC | 105 |
A For Aluminum and titanium alloys hardness values are for information only.
B Aluminum alloy 2024-T4 shall be supplied in naturally aged condition. This material is not recommended for nuts in sizes greater than 1/4 ( 0.250) inch.
| Product | Proof Stress, ksi | Test Conducted Using Full Size Product | |
|---|---|---|---|
| Jam, slotted and castle nuts | All | A | -- |
| All other nuts | Up to 120 | -- | A |
| All other nuts | Over 120 | A | -- |
A Mandatory Tests.
| Nominal Size, inch. | Coarse Threads - UNC | Fine Threads - UNF | 8 Thread Series - 8UN | |||
|---|---|---|---|---|---|---|
| Threads / inch | Stress AreaA, in2 | Threads / inch | Stress AreaA, in2 | Threads / inch | Stress AreaA, in2 | |
| 1/4 | 20 | 0.0318 | 28 | 0.0364 | -- | -- |
| 5/16 | 18 | 0.0524 | 24 | 0.0580 | -- | -- |
| 3/18 | 16 | 0.0775 | 24 | 0.0878 | -- | -- |
| 7/16 | 14 | 0.1063 | 20 | 0.1187 | ||
| 1/2 | 13 | 0.1419 | 20 | 0.1599 | ||
| 9/16 | 12 | 0.1820 | 18 | 0.2030 | ||
| 5/8 | 11 | 0.2260 | 18 | 0.2560 | ||
| 3/4 | 10 | 0.3340 | 16 | 0.3730 | ||
| 7/8 | 9 | 0.4620 | 14 | 0.5090 | ||
| 1 | 8 | 0.6060 | 12 | 0.6630 | ||
| 1 1/8 | 7 | 0.7630 | 12 | 0.8560 | 8 | 0.790 |
| 1 1/4 | 7 | 0.9690 | 12 | 1.0730 | 8 | 1.000 |
| 1 3/8 | 6 | 1.1550 | 12 | 1.3150 | 8 | 1.233 |
| 1 1/2 | 6 | 1.4050 | 12 | 1.5810 | 8 | 1.492 |
A Tensile stress areas are computed using the following formula: As = 0.7854 [D- (0.9743/n)]2
Where:
As = Tensile stress area, in.2,
D = Nominal size (basic major diameter), in., and,
n = number of threads per inch.
| Alloy | Test Method |
|---|---|
| Copper | E52, E54, E62, E75, E478 |
| Aluminum | E34, E101, E227 |
| Nickel | E38, E76, E354 |
| Titanium | E120, E1409 |